ISO 18610:2016 specifies an ultrasonic method to determine the components of the elasticity tensor of ceramic matrix composite materials at room temperature. Young's moduli shear moduli and Poisson coefficients, can be determined from the components of the elasticity tensor.

It applies to ceramic matrix composites with a continuous fibre reinforcement: unidirectional (1D), bidirectional (2D), and tridirectional (×D, with 2 < × ≤ 3) which have at least orthotropic symmetry, and whose material symmetry axes are known.

This method is applicable only when the ultrasonic wavelength used is larger than the thickness of the representative elementary volume, thus imposing an upper limit to the frequency range of the transducers used.


Общая информация 

  • Текущий статус
     : Опубликовано
    Дата публикации
     : 2016-09
  • Версия
     : 1
  • Технический комитет
     : ISO/TC 206 Fine ceramics
  • ICS
     :
    81.060.30 Advanced ceramics

Приобрести данный стандарт

Формат Язык
PDF
Бумажный
  • CHF124

Жизненный цикл

Цели в области устойчивого развития

Данный стандарт разработан для достижения следующих Цель устойчивого развития

9
Индустриализация, инновации и инфраструктура

Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

  2. Интернет-магазин
  3. Каталог стандартов
  4. МКС
  5. 81
  6. 81.060
  7. 81.060.30
  8. ISO 18610:2016