ISO 15653:2018 specifies methods for determining fracture toughness in terms of stress intensity factor (K), crack tip opening displacement or CTOD (δ) and experimental equivalent of the J-integral for welds in metallic materials (J).
ISO 15653:2018 complements ISO 12135, which covers all aspects of fracture toughness testing of parent metal and which needs to be used in conjunction with this document. This document describes methods for determining point values of fracture toughness. It should not be considered a way of obtaining a valid R-curve (resistance-to-crack-extension curve). However, the specimen preparation methods described in this document could be usefully employed when determining R-curves for welds. The methods use fatigue precracked specimens which have been notched, after welding, in a specific target area in the weld. Methods are described to evaluate the suitability of a weld for notch placement within the target area, which is either within the weld metal or within the weld heat-affected zone (HAZ), and then, where appropriate, to evaluate the effectiveness of the fatigue crack in sampling these areas.
Status: PublishedPublication date: 2018-01
Edition: 2Number of pages: 46
Technical Committee: ISO/TC 164/SC 4 Fatigue, fracture and toughness testing
- ICS :
- 25.160.40 Welded joints and welds
Buy this standard
|std 1 166||PDF + ePub|
|std 2 166||Paper|
A standard is reviewed every 5 years
Stage: 90.60 (Under review)
Got a question?
Check out our FAQs
Monday to Friday - 09:00-12:00, 14:00-17:00 (UTC+1)
Keep up to date with ISO
Sign up to our newsletter for the latest news, views and product information.