This part of ISO 898 specifies mechanical and physical properties of nuts with coarse thread and fine pitch
thread made of carbon steel and alloy steel when tested at an ambient temperature range of 10 °C to 35 °C.
Nuts conforming to the requirements of this part of ISO 898 are evaluated at that ambient temperature range.
It is possible that they do not retain the specified mechanical and physical properties at elevated and/or lower
temperatures.
NOTE 1 Nuts conforming to the requirements of this part of ISO 898 have been used in applications
ranging from ?50 °C to +150 °C. It is the responsibility of users to consult an experienced fastener materials expert
for temperatures outside the range of ?50 °C to +150 °C and up to a maximum temperature of +300°C to determine
appropriate choices for a given application.
NOTE 2 Information for the selection and application of steels for use at lower and elevated temperatures is given for
instance in EN 10269, ASTM F2281 and in ASTM A320/A320M.
This part of ISO 898 is applicable to nuts:
a) made of carbon steel or alloy steel;
b) with coarse thread M5 ≤ D ≤ M39, and fine pitch thread M8×1 ≤ D ≤ M39×3;
c) with triangular ISO metric thread according to ISO 68-1;
d) with diameter/pitch combinations according to ISO 261 and ISO 262;
e) with specified property classes, including proof load;
f) with different nut styles: thin nuts, regular nuts and high nuts;
g) with minimum height m ≥ 0,45D;
h) with a minimum outside diameter or width across flats s ≥ 1,45D (see Annex A);
i) able to mate with bolts, screws and studs with property classes according to ISO 898-1.
For hot dip galvanized nuts, see ISO 10684.
This part of ISO 898 does not specify requirements for properties such as:
— prevailing torque properties (see ISO 2320);
— torque/clamp force properties (see ISO 16047 for test method);
— weldability;
— corrosion resistance.
Общая информация
-
Текущий статус: ОтозваноДата публикации: 2012-03Этап: Отмена международного стандарта [95.99]
-
Версия: 3
-
Технический комитет :ISO/TC 2/SC 12ICS :21.060.20
- RSS обновления
Жизненный цикл
-
Ранее
ОтозваноISO 898-2:1992
ОтозваноISO 898-6:1994
-
Сейчас
-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
-
Пересмотрен
ОпубликованоISO 898-2:2022